Formation of LaFeO3 and thermal decomposition reactions in lanthanum(III) oxalate-iron(II) oxalate crystalline mixture
Formation of LaFeO3 and thermal decomposition reactions in lanthanum(III) oxalate-iron(II) oxalate crystalline mixture
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : Thermal processes involved during the decomposition course of La 2(C2O4)3•10H 2O-FeC2O4•2H2O (1:2 mole ratio) mixture up to 750 °C, in an atmosphere of air, were monitored by thermogravimetry and differential thermal analysis. X-ray diffraction and Mössbauer spectroscopy were used to characterize the intermediates and the final product. The results showed that a microcrystalline or possibly amorphous iron(III) oxide with a paramagnetic nature was appeared in the early stages of decomposition at 250 °C. By increasing the temperature, a well crystalline hematite with ferromagnetic properties was obtained. XRD pattern of the mixture calcined at 1100 °C shows the formation of LaFeO3 single phase in consistent with the hyperfine magnetic splitting (one sextet of lines) characteristic of LaFeO3 obtained in the Mössbauer spectra of the mixture calcined at the same temperature. 
ردمد : 0022-2461 
اسم الدورية : Journal of Materials Science 
المجلد : 41 
العدد : 22 
سنة النشر : 1427 هـ
2006 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, December 28, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
M A GabalGabal, M Aباحثدكتوراهmgabalabdo@yahoo.com
Samy S Ata-AllahAta-Allah, Samy Sباحثدكتوراه 
عبدالرحمن عبيد اليوبيAl-Youbia, Abdulrahman Obaidباحثدكتوراهaalyoubi@kau.edu.sa
سليمان ناصر باسهلBasahel, Suliman Naserباحثدكتوراهsbasahel@kau.edu.sa
شعيل أحمد الثبيتيAL-Thabaitia, Shaeel Ahmedباحثدكتوراهsthabiti@hotmail.com

الملفات

اسم الملفالنوعالوصف
 31843.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث